autogenous shrinkage

基本解释

• [土木建筑工程]自收缩自生收缩量
• [交通运输工程]自收缩

英汉例句

双语例句

• The tensile stress induced by restrained thermal and autogenous shrinkage deformations was the main driving force of cracking in concrete at early age.
  温度变形和自生收缩变形等受约束形成的拉应力，是引起混凝土早期开裂的主要驱动力；
• By these experience, the paper firstly brought forward three concepts: turning point of autogenous shrinkage of concrete, continue maintain time, fly ash concrete strength balanced point.
  通过试验研究文中首次提出了三个概念：混凝土自生收缩的转折点、继续养护时间、粉煤灰混凝土强度平稳点。
• The experimental results show that SCA could either restrain the early autogenous shrinkage of paste or improve the prolonged shrinkage of concrete.
  结果表明：复合矿物外加剂可抑制混凝土自收缩变形，并使混凝土长期收缩变形得到补偿。

• autogenous shrinkage更多例句

词组短语

短语

• autogenous -shrinkage ratio 自收缩率
• autogenous shrinkage ratio 自收缩率
• autogenous shrinkage strain 自收缩应变
• autogenous shrinkage stress 自收缩应力
• early autogenous shrinkage 早期收缩的

• autogenous shrinkage更多词组

专业释义

土木建筑工程

• 自收缩

  At the primeval moulded time, cracks are mainly caused by temperature shrinkage and autogenous shrinkage, after that, it is mostly caused by dry shrinkage.
  混凝土浇筑初期开裂主要是温度变形和自收缩引起，后期开裂则主要是因干缩所致。

• 自生收缩量

交通运输工程

• 自收缩

  The research contents include that the early chemical shrinkage of cement paste, the early autogenous shrinkage of UFA highway concrete, the early plastic shrinkage, the early thermal shrinkage and all age dry-shrinkage.
  其中包括水泥浆体的早期化学收缩变形以及UFA公路混凝土早期的自收缩变形、塑性收缩变形、温度收缩变形以及各龄期的干燥收缩变形等。